LG PMMA IF870S
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | LG MMA Corp. |
| Trademark: | LG PMMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GIw52K_LG-PMMA-IF870S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PMMA IF870S is a Polymethyl Methacrylate Acrylic material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG PMMA IF870S are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 3300 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) | 1.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 1 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 2 | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.10 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.050 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 0.10 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | 4000 V/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-341U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| TAROLOX 10 H G6 DX0 | Taro Plast S.p.A. | PBT | TAROLOX |
| TRIBOCOMP® PPS GF30 TS0 | EPIC Polymers | PPS | TRIBOCOMP® |
| XYRON™ X1561 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Hostacom EKC 133N KF C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |