Marlex® K605
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GImAHg_Marlex-K605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® K605 is a High Density (HMW) Polyethylene material. It is available in Latin America or North America for blow molding or thermoforming. Important attributes of Marlex® K605 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 11 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded, F50) | 30.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 1510 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 4(Compression Molded) | 240 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 88.0 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 5 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Type S bar |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| API PS 645-21 | American Polymers, Inc. | PS (HIPS) | API PS |
| DuraSurf™ 2001 DuraJet | Crown Plastics | UHMWPE | DuraSurf™ |
| Geon™ Vinyl Rigid Extrusion 85857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Karina YELLOW COLOR CONCENTRATE -E 02/127-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LIM6900-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |