COSMOPLENE® H101E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GIXlgw_COSMOPLENE-H101E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE H101E is Polypropylene Homopolymer designed for high stiffness and tensile strength. COSMOPLENE H101E is specially designed as medium flow, high toughness grade for industrial application like automotive parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 46.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 830 | % | ASTM D638 |
| Flexural Modulus | 1370 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.9 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 165 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Pressure | 6.86 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1980 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RELENE® C 31101 | Reliance Industries Limited | HDPE | RELENE® |
| ALKAMIX™ MB6002 | Qenos Pty Ltd | LLDPE | ALKAMIX™ |
| DynaStat® 1857 | Polymer Dynamix | Acetal (POM) Copolymer | DynaStat® |
| Golden Compound PP S²PC 3545 BO 15IM16 | Golden Compound GmbH | PP, Unspecified | Golden Compound |