HAIPLEN EP50 T3
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GIISqT_HAIPLEN-EP50-T3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer 16% mineral filled, high flow, good stiffness/impact balance. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D), anti-static (AS), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | |
| Across Flow | 1.1 | % | |
| Granule Humidity | 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 21.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 16 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1850 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ASTM D256, ISO 179 | |
| Notched Izod Impact | 45 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 108 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 56.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 68.0 | °C | ASTM D1525, ISO 306/B 3 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 HI SI HF | RTP Company | PP Copolymer | RTP |
| RONFALIN® C C130 | A. Schulman Europe | PC+ABS | RONFALIN® C |
| ALTECH® PA6 A 2015/321 GF15 UV IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Ebalta Xiameter RTV 3481 | Ebalta Kunststoff GmbH | Silicone Rubber, RTV-1 | Ebalta |
| LNP™ THERMOCOMP™ MFB63 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |