EQUATE PE EFDA-7047
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | EQUATE Petrochemical Company KSCC |
| Trademark: | EQUATE PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GIGcGS_EQUATE-PE-EFDA-7047.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EFDA-7047 is a linear low-density polyethylene (LLDPE) resin for tubular blown film extrusion. Films made from this resin have good toughness, high tensile strength and puncture resistance. EFDA-7047 does not contain any slip or antiblocking agent. APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Bulk Density | 538 | kg/m³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 193 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 34.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 26.0 | MPa | ASTM D882 |
| Dart Drop Impact (Blown Film) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 µm | 35.0 | kN/m | ASTM D1922 |
| TD : 25.0 µm | 135.0 | kN/m | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Energy (25.0 µm) 2 | 700 | J/cm | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 210 | °C |
| Extrusion instructions |
|---|
| Die Gap: >1.8 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8328-65FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Thermylene® P6-20FG-0693 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| WanBlend® WHT-890E5 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| GAPEX® RPP40EU29UL-NA | Ferro Corporation | PP, Unspecified | GAPEX® |
| SCHULAKETON GF10 | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |