OmniCarb™ PC GR10 CBFR0
| Category: | PC , Polycarbonate |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GI6c7n_OmniCarb-PC-GR10-CBFR0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced, Chlorine & Bromine Free, Flame Resistant Polycarbonate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 135 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 293 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 65.6 to 121 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 SI 2 | RTP Company | PC | RTP |
| Taitacell EPS-361T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Gravi-Tech™ GRV-UR-080-W | PolyOne Corporation | PUR, Unspecified | Gravi-Tech™ |
| LUVOCOM® 1-8840 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| SECCO S2040 | Shanghai SECCO Petrochemical Co., Ltd | PP Homopolymer | SECCO |