POLYFLAM® RIPP 2000
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GHdFkG_POLYFLAM-RIPP-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled flame retardant PP-Copolymer grade, halogen free acc. DIN VDE 0472 part 815, fulfills french norm NF P 92 - 501/505 class M2 |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.5 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 46 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/A50 |
| -- | 64.0 | °C | ISO 306/B50 |
| Ball Pressure Test (120°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 1.50 mm, Self-Extinguishing | 0.0 | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | mm/min | |
| Flame Rating | |||
| 1.50 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-2 | UL 94, IEC 60695-11-10, -20 | |
| 0.750 mm | V-2 | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 700 | °C | |
| 1.50 mm | 700 | °C | |
| 3.00 mm | 700 | °C | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic PFA 6503PAZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| Chemlon® 240 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| EnCom GF ABS10 | EnCom, Inc. | ABS | EnCom |
| MAJORIS DC400 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| PALMID® R 66 S | pal plast GmbH | Nylon 66 | PALMID® |