LUVOCOM® 1104-8928 Datasheet,PEK,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1104-8928 is a polyether ketone (PEK) material that contains a mineral filler. This product is available in Europe,. LUVOCOM®The main features of 1104-8928 are: Flame Retardant anti-warping chemical resistance Typical application areas include: engineering/industrial accessories Automotive Industry

General Information
Filler / Reinforcement	Mineral filler
Features	Low warpage Good chemical resistance Flame retardancy
Uses	Engineering accessories Application in Automobile Field Cam
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.33	g/cm³	ISO 1183
Molding Shrinkage	1.0 - 1.6	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5000	MPa	ISO 527-2
Tensile Stress (Break)	90.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.3	%	ISO 527-2
Flexural Modulus	4500	MPa	ISO 178
Flexural Stress	170	MPa	ISO 178
Flexural Strain at Flexural Strength	6.8	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	280	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	162	°C	ISO 75-2/A
Continuous Use Temperature	260	°C	UL 746B
Vicat Softening Temperature	300	°C	ISO 306/A
CLTE - Flow	4.7E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.25	W/m/K	DIN 52612

Injection	Nominal Value	Unit
Drying Temperature
Dehumidification desiccant, B	150	°C
Hot air dryer, A	140	°C
Drying Time
Dehumidification desiccant, B	4.0 - 8.0	hr
Hot air dryer, A	4.0 - 16	hr
Suggested Max Moisture	0.050	%
Rear Temperature	370 - 390	°C
Middle Temperature	380 - 420	°C
Front Temperature	390 - 420	°C
Nozzle Temperature	390 - 420	°C
Processing (Melt) Temp	390	°C
Mold Temperature	180 - 220	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PEK , Polyether Ketone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GHUYv2_LUVOCOM-1104-8928.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Adell PS IF-110	Adell Plastics, Inc.	PS (HIPS)	Adell PS
AQUAFORCE® PA66 G30-01 SCHWARZ	LEIS Polytechnik - polymere Werkstoffe GmbH	Nylon 66	AQUAFORCE®
ExxonMobil™ PP3155E3	ExxonMobil Chemical	PP Homopolymer	ExxonMobil™
Kepital® F15-33	Korea Engineering Plastics Co., Ltd	Acetal (POM) Copolymer	Kepital®
ISPLEN® PM 281 BV	REPSOL	PP Copolymer	ISPLEN®