PC-COM™ PC415-50
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Compounders Limited |
| Trademark: | PC-COM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GHTk53_PC-COM-PC415-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC-COM PC415-50 is a medium flow general purpose polycarbonate grade with UV absorption. Applications include automotive interior covers and lighting. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/50 |
| Break | 120 | % | ISO 527-2 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed | 124 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Velocity | 65 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3783 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 2700 S-50A MD NATURAL | RTP Company | SEBS | RTP |
| Petro Rabigh PE M8060U | Rabigh Refining & Petrochemical Co. | HDPE | Petro Rabigh PE |
| TORZEN® HV80A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| OTECH TPE OTO9588 - Power Insulation | OTECH Corporation | TPE | OTECH TPE |