Trithene® TX 4003
| Category: | LDPE+LLDPE , Low Density Polyethylene + LLDPE |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GH4yh4_Trithene-TX-4003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TX 4003 is a low density polyethylene LLDPE material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TX 4003 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 120 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 130 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 380 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 770 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 140 | g | ASTM D1922 |
| TD : 50 µm, blown film | 270 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 63 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 16 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Teor de Linear, PTN-736-Q: 22.5% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 185 | °C | |
| Cylinder Zone 2 Temp. | 180 - 195 | °C | |
| Cylinder Zone 3 Temp. | 200 - 210 | °C | |
| Adapter Temperature | 210 - 225 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1Recommended Die Gap: 0.8 to 1.7 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer Z85B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| FlexFoam-It® X | Smooth-On, Inc | PUR, Unspecified | FlexFoam-It® |
| Jamplast JPEVA18 | Jamplast, Inc. | EVA | Jamplast |
| RTP 199 X 143684 A | RTP Company | PP, Unspecified | RTP |
| ADVANCENE™ EM-5822-AAH | ETHYDCO | HDPE | ADVANCENE™ |