LNP™ LUBRICOMP™ ECL36 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGtSGQ_LNPLUBRICOMPECL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ECL36 is a compound based on Polyetherimide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound ECL-4036 Product reorder name: ECL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 4.00 - 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 1.1 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.25 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.32 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 18500 | MPa | ISO 178 |
| 80°C | 17900 | MPa | ISO 178 |
| 120°C | 17400 | MPa | ISO 178 |
| 150°C | 16400 | MPa | ISO 178 |
| 200°C | 15300 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 256 | MPa | ISO 178 |
| 80°C | 214 | MPa | ISO 178 |
| 120°C | 182 | MPa | ISO 178 |
| 150°C | 145 | MPa | ISO 178 |
| 200°C | 91.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.39 | ASTM D3702 Modified | |
| With Self-Static | 0.48 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 1.6 | % | ISO 178 |
| 80°C | 1.5 | % | ISO 178 |
| 120°C | 1.4 | % | ISO 178 |
| 150°C | 1.6 | % | ISO 178 |
| 200°C | 1.0 | % | ISO 178 |
| Wear Factor - Washer | 31.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C 3 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 4 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -40°C | 25 | kJ/m² | ISO 180/1U |
| 23°C | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1890 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.33 | W/m/K | ASTM D5930 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DAI-EL™ G-7452 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Eco Cool Plus CMP 05 | EcolBiotech Co., Ltd | PLA | Eco Cool Plus |
| Lion Idemitsu Composites PPS G142Z1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| PLUSTEK PB300G2 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| KMI PP KM-099IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |