Romiloy® 4010/02 GF 8
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGgLiP_Romiloy-4010-02-GF-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Romiloy®4010/02 GF 8 is an acrylonitrile butadiene styrene + nylon (ABS + nylon) material, and the filler is 8.0% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. Romiloy®The main characteristics of 4010/02 GF 8 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2550 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.The value listed as Coefficient of Linear Thermal Expansion ISO 11359-1, was tested in accordance with DIN 53752Tensile Strain @ Break, DIN EN ISO 527, 50 mm/min, 23°C: >30% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 67-01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| SCHULABLEND® (PMMA/PC) M/MP K6001 V1 TIEFSCHWARZ | A. Schulman Europe | PC+Acrylic | SCHULABLEND® |
| Ultramid® A27 E 01 | BASF Corporation | Nylon 66 | Ultramid® |
| Ducor® 2340 RC | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| Kepamid® 1325GVS | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |