Fortron® 0205
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGawrU_Fortron-0205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 0205 is an easy flowing unfilled grade. It demonstrates excellent chemical resistance and thermal stability. Intended for compounding with various fillers. Available standard in pellet (0205P4) and powder (0205B4) form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Specific Volume | 0.715 | cm³/g | ASTM D792 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1830 | J/kg/°C | Internal method |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | |||
| Flow | 1.0 - 1.2 | % | ASTM D955 |
| Transverse flow | 0.80 - 1.0 | % | ASTM D955 |
| Vertical flow direction | 1.5 - 1.8 | % | ISO 294-4 |
| Flow direction | 1.2 - 1.5 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 93 | ASTM D785 | |
| M scale | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 86.2 | MPa | ASTM D638 |
| Fracture | 66.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 3900 | MPa | ISO 178 |
| Flexural Stress 1 | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 95.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| Arc Resistance | 124 | sec | ASTM D495 |
| Comparative Tracking Index | 100 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 300 - 310 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Nozzle Temperature | 300 - 310 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 40.0 - 80.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 60.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 310 to 320°CZone 4 Temperature: 310 to 320°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3605 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| KPOL-LLDPE LL K-1.1/918 | KPOL Chem Co. | LLDPE | KPOL-LLDPE |
| KOCETAL® K200BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| INSPIRE™ 227 | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |
| Karina GRAY PVC COMPOUND 950-18/277-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |