Generic PBT - Glass\Mineral
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGZyug_Generic-PBT---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PBT - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.61 - 1.78 | g/cm³ | ASTM D792 |
| 23°C | 1.61 - 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 - 0.62 | % | ASTM D955 |
| Transverse flow : 23°C | 0.50 - 0.71 | % | ASTM D955 |
| 23°C | 0.31 - 1.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.083 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 109 - 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7200 - 13500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 72.4 - 101 | MPa | ASTM D638 |
| Fracture, 23°C | 89.4 - 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 - 3.0 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5380 - 10300 | MPa | ASTM D790 |
| 23°C | 9350 - 11100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 120 - 159 | MPa | ASTM D790 |
| 23°C | 129 - 182 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 - 7.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 36 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 42 - 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 240 - 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 204 - 216 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 209 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 193 - 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 189 - 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 - 220 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow | 2.0E-5 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 - 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 2.0E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 18 - 30 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 3.30 - 4.30 | ASTM D150 | |
| 23°C | 3.71 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.020 | ASTM D150 | |
| 23°C | 2.0E-3 - 0.040 | IEC 60250 | |
| Arc Resistance | 124 - 140 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 - 126 | °C | |
| Drying Time | 2.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.034 | % | |
| Rear Temperature | 235 - 252 | °C | |
| Middle Temperature | 245 - 255 | °C | |
| Front Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 250 - 263 | °C | |
| Processing (Melt) Temp | 247 - 266 | °C | |
| Mold Temperature | 75.0 - 90.0 | °C | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 65 - 100 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PBT - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 7104 | Chevron Phillips Chemical Company LLC | LLDPE | Marlex® |
| Maxelast® P3785H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| MAXAMID™ N66TF10-BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| RAMTAL PM7013G2 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| Nypol® PA A3 ST NTLA010 NR385 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |