Nypol® PA A3 G38 HS UV RH PRTA011 NR447
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGZZ58_Nypol-PA-A3-G38-HS-UV-RH-PRTA011-NR447.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in color black reinforced with 38% of fiberglass, heat stabilized, resistivity hydrolysis and UV good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.70 | % | ASTM D570 |
| Ash Content | 36 to 40 | % | ASTM D2584 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6620 | MPa | ASTM D790 |
| Flexural Strength | 183 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 255 | °C | |
| 1.8 MPa, Unannealed | 235 | °C | |
| Melting Temperature | 250 to 265 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC14-1213L | Spartech Polycom | Nylon 66 | Spartech |
| Cheng Yu ML1210 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| GERMAMID 6 GK 30 HZ-6662 | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| Sylvin 6245-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wanthane® WHT-1189B | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |