Order Products : sales@su-jiao.com
Andur 9-5 APLF/Curene® 442
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGFWhP_Andur-9-5-APLF-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 9-5 APLF is a polyester based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 94 to 97 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442, other diamines or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 96 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 1.62 | MPa | ASTM D695 |
| 10% strain | 5.67 | MPa | ASTM D695 |
| 15% strain | 9.14 | MPa | ASTM D695 |
| 20% strain | 13.8 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 11.0 | MPa | ASTM D412 |
| 300% strain | 17.2 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 51.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 500 | % | ASTM D412 |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 4.0 - 5.0 | min | |
| Demold Time (100°C) | 20 | min | |
| Post Cure Time (100°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 94 to 97Die C Tear, ASTM D1004: 500 pliAverage Split Tear, ASTM D1938: 300 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 9-5 APLF: 160-180°F Curene 442: 230-240°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A RV250K AE 121 C NAT 3489 | Radici Plastics | Nylon 66 | Radiflam® |
| Sarlink® TPE EE-2250N NAT | Teknor Apex Company | TPE | Sarlink® TPE |
| Karina CLEAR PVC COMPOUND -E 75/313-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Hostacom X M3 V05 102942 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9413-85UV Clear 876 | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |