Epocast 50-A1/946
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGFFtg_Epocast-50-A1-946.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 50-A1 Resin/Hardener 946 epoxy laminating system is an unfilled, solvent-free, easy-to-handle material for the manufacture or repair of composite structures as well as for filament winding. Epocast ® 50-A1 resin/Hardener 946 epoxy laminating system is self extinguishing. Epocast ® 50-A1 / Hardener 946 is qualified to BMS 8-201, Type IV, Rev. F. This product is also available in a longer work life version - Epocast ® 50-A1 resin/Hardener 9816 epoxy laminating system. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- 2 | 1.21 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | ASTM D695 | ||
| -- 3 | 23.6 | MPa | ASTM D695 |
| -- 4 | 25.2 | MPa | ASTM D695 |
| -- 5 | 27.9 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| -- 6 | 349 | MPa | ASTM D695 |
| -- 7 | 333 | MPa | ASTM D695 |
| -- 8 | 317 | MPa | ASTM D695 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | FAR 25.853(a) | ||
| burn length | mm | FAR 25.853(a) | |
| drip extinguishing time | 0.0 | hr | FAR 25.853(a) |
| self extinguishing time | 0.0 | hr | FAR 25.853(a) |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 15 | ||
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C | 2400 | cP | ASTM D2196 |
| 25°C 9 | 400 | cP | ASTM D2196 |
| 25°C 10 | 7770 | cP | ASTM D2196 |
| Additional Information |
|---|
| CURE SCHEDULE: Five days at 77°F (25°C) or two hours at 170-200°F (77-93°C) after room temperature gel. Handling and machining may be done after 8-16 hours at room temperature. |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Cure 27 days at 77°F |
| 4 . | Cure 1 day at 77°F + 2 hr. at 150°F |
| 5 . | Cure 7 days at 77°F |
| 6 . | Cure 27 days at 77°F |
| 7 . | Cure 1 day at 77°F + 2 hr. at 150°F |
| 8 . | Cure 7 days at 77°F |
| 9 . | Hardener |
| 10 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane TC-885 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Filter-bond™ R-30-6 | Hapco Inc. | TS, Unspecified | Filter-bond™ |
| Generic ASA+PC | Generic | ASA+PC | Generic |
| Petrothene® NA420000 | LyondellBasell Industries | LDPE+EVA | Petrothene® |
| POLYFLON™ F-131 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |