Clariant Nylon 6 PA-211X012
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GG4Geu_Clariant-Nylon-6-PA-211X012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6 PA-211X012 is a polyamide 6 (nylon 6) material,. This product is available in North America and is processed by extrusion or injection molding. The main features of the Clariant Nylon 6 PA-211X012 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.3 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 40 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 200 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength | 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.1 | °C | ASTM D648 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 249 - 274 | °C | |
| Middle Temperature | 249 - 274 | °C | |
| Front Temperature | 249 - 274 | °C | |
| Processing (Melt) Temp | 254 - 271 | °C | |
| Melt Temperature (Aim) | 266 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 180°FScrew Speed Target: 75 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide RF006S-GY9A121 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Sylvin 8672-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Armlen® PP CM 25.1 | Poly Plastic | PP, Unspecified | Armlen® |
| Iupital® FC2020H | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Sylvin 7844-80 Red 604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |