LNP™ LUBRICOMP™ FL003 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GG2i1A_LNP-LUBRICOMP-FL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound FL-4030 Product reorder name: FL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1480 | MPa | ASTM D638 |
| -- | 1310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 24.0 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/5 |
| Break 3 | 14.0 | MPa | ASTM D638 |
| Break | 12.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 8.5 | % | ASTM D638 |
| Yield | 8.4 | % | ISO 527-2/5 |
| Break 5 | 59 | % | ASTM D638 |
| Break | 240 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 851 | MPa | ASTM D790 |
| -- 7 | 922 | MPa | ISO 178 |
| Flexural Stress | 20.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 8 | 3.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 95 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.30 | J | ASTM D3763 |
| -- | 4.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 72.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 82.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 46.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 46.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.3E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.5E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 230 | °C | |
| Mold Temperature | 40.0 to 55.0 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® HT 70 | API SpA | SEBS | megol® |
| BIOH™ Polyol X-0210 | Cargill Industrial Bio-Products | Biodeg Polymers | BIOH™ Polyol |
| Dryflex® XP 0801 | ELASTO | TPE | Dryflex® |
| Greene 209 | Greene, Tweed & Co. | NBR | Greene |
| Karina RED COLOR CONCENTRATE 42/268-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |