PENTAMID AB MA30T H grau 7035/1
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFlK3w_PENTAMID-AB-MA30T-H-grau-7035-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66+6, 30% mineral filled, good surfaces, special coloration |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.85 | -- | % | ISO 294-4 |
| Flow direction | 0.70 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.9 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 180 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5900 | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 11 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 29 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA66+PA6, MHRC, 14-060 N, MD30The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA66+PA6, MHRC, 14-060 N, MD30 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 275 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 65.0 | MPa | |
| Holding Pressure | 35.8 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2620PB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| FLEXCHEM™ 5052 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| INDURE™ X220 | LyondellBasell Industries | TPO (POE) | INDURE™ |
| MACOMASS PP MM-PP HG 82 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| SABIC® LDPE 2502X0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |