Lionpol HF-208218
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Lion Polymers Incorporated |
| Trademark: | Lionpol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFUkCX_Lionpol-HF-208218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lionpol HF-208218 is a thermoplastic elastomer (TPE) product,. It is available in North America. The main characteristics are: high liquidity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 82 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.8 - 2.0 | % | ASTM D955 |
| Transverse flow | 1.8 - 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 18 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.262 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.92 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1100 | % | ASTM D412 |
| Additional Information |
|---|
| Permanent Set: 20% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 141 - 179 | °C | |
| Front Temperature | 163 - 202 | °C | |
| Nozzle Temperature | 163 - 202 | °C | |
| Mold Temperature | 21.1 - 32.2 | °C | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2765 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SCLAIR® 8107 | NOVA Chemicals | LLDPE | SCLAIR® |
| Nanjing Hongrui PP P3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Polifil® PP RMT-10 | The Plastics Group | PP Impact Copolymer | Polifil® PP |
| TOTAL Polyethylene Bio TPSeal® 0750_05 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |