AKROMID® B3 LA black (4056)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFOFS9_AKROMID-B3-LA-black-4056-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 LA black (4056) is a unreinforced, laser markable polyamide 6 Applications are handles, housings and covering parts for the automotive industry and power tools. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.1 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.5 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 6.5 | -- | % | ISO 178 |
| Tensile Modulus | 3400 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 20 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 3000 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 115 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 3.0 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 62 T 40 | SILON s.ro | PP Homopolymer | TABOREN |
| X-Pro SP 200 P 4058 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| LNP™ VERTON™ RVL29ESS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |
| Lucel® FW700S | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| HiFill® PP LGF30 2000 BK 12MM | Techmer Engineered Solutions | PP, Unspecified | HiFill® |