LNP™ THERMOTUF™ WF003I compound
| Category: | PBT , Thermoplastic Polyester |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFHFhb_LNPTHERMOTUFWF003Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* WF003I is a compound based on PBT resin containing 15% Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound WF003I Product reorder name: WF003I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.11 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4920 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4350 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 133 | MPa | ISO 178 |
| -- 4 | 119 | MPa | ISO 178 |
| Flexural Strain at Break 5 | 5.7 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | 209 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 180 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282H | RTP Company | Nylon 66 | RTP |
| Pro-Comp™ PPHGF30-E | Southland Polymers | PP Homopolymer | Pro-Comp™ |
| RheTech Polypropylene M15P101-01A | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Sylvin 8808-70D Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Karina BLUE PVC COMPOUND 800-06/230-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |