Durethan® DP AKV 30 FN00 DUS013 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFFp8L_Durethan-DP-AKV-30-FN00-DUS013-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30 % glass fibers, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 270°C, 2.00 mm 1 | 0.70 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 270°C, 2.00 mm 3 | 0.20 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 120 | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 5.1 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 9300 | 5600 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | -- | 120 | MPa | |
| 23°C 6 | 190 | 120 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 2.7 | 4.8 | % | ISO 178/A |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 45 | 47 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 224 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 3.0E+16 | 4.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 5.0E+15 | 5.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 39 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 3.90 | 8.70 | ||
| 23°C, 1 MHz | 3.70 | 4.10 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 8.0E-3 | 0.13 | ||
| 23°C, 1 MHz | 0.012 | 0.070 | ||
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | ||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 265 to 285 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 2200 | POLY GIN | PC | MARCOBLEND |
| Cevian® K160 | PlastxWorld Inc. | Acrylic, Unspecified | Cevian® |
| Cevian®-V VCF20 (Type C) | Daicel Polymer Ltd. | ABS | Cevian®-V |
| InnoTuf® HP-2190A | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Karina IVORY PVC COMPOUND 951-35/4-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |