ETILINAS PC4012
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | POLYETHYLENE MALAYSIA SDN BHD |
| Trademark: | ETILINAS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GEWRE9_ETILINAS-PC4012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ETILINAS PC4012 is designed specifically for coating of metal pipes and tubes. ETILINAS PC4012 is based on a special high density copolymer with excellent resistance to environmental stress cracking, and contains suitable additives for ease of coating manufacture and to ensure long term weathering resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2/2 |
| Flexural Modulus | 850 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -100 | °C | ASTM D746 |
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Density of Compound, ISO 1872/1, Annealed: 953 kg/m³Carbon Black Content, ISO 6964: 2.25%Thermal Conductivity, BS 874, 23°C: 0.4 W/m/°COxidation Induction Time, ISO TR10837, 210°C: >20 min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 225 | °C |
| Extrusion instructions |
|---|
| Suggested Screen Pack: 40/80 Mesh |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane TC-262 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Evoprene™ G 3315 | AlphaGary | SEBS | Evoprene™ G |
| Lasulf LASULF G/20 | LATI S.p.A. | PSU | Lasulf |
| Karina WHITE PVC COMP E-854-10/390-B-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLIMAXX 1111NXBA4 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |