Retpol® CD 10 HS UV3
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GEPcy2_Retpol-CD-10-HS-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCOMP CD 10 HS UV3 is an unfilled polypropylene copolymer compound. It has been developed for rigid mouldings requiring good impact resistance along with the low SG of an unfilled material. It has been stabilized to meet automotive heat aging requirements and for continual exposure to UV radiation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 70 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 71 | ||
| Shore D, 15 sec, 3.00 mm | 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 250 | % | ASTM D638 |
| Flexural Modulus (6.00 mm) | 1020 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.00 mm) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.00 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 110 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 10.2.0 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| tefanyl® VE VEIP 250 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| Niuk 60GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | PBT | Niuk |
| Aaroprene® ATPR 2000 60A | Aaron Industries Corp. | TPE | Aaroprene® |
| Ultramid® Structure B3WG10 LFX BK23215 | BASF Corporation | Nylon 6 | Ultramid® |