Lustran® ABS 682
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GE91AF_Lustran-ABS-682.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran ABS 682 is a high performance, HCFC-141b resistant grade of ABS for injection molded refrigerator and freezer components. As with any product, use of Lustran ABS 682 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 5.2 | g/10 min | ASTM D1238, ISO 1133 |
| 230°C/10.0 kg | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| 230°C/3.8 kg | 0.70 | g/10 min | ASTM D1238 |
| 220°C/3.8 kg | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2470 | MPa | ASTM D638 |
| -18°C | 2810 | MPa | ISO 527-2/1 |
| 23°C | 2420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 43.0 | MPa | ASTM D638 |
| Yield, -18°C | 64.0 | MPa | ISO 527-2/50 |
| Yield, 23°C | 48.0 | MPa | ISO 527-2/50 |
| Break | 32.0 | MPa | ASTM D638 |
| Break, -18°C | 52.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break | 34 | % | ASTM D638 |
| Break, -18°C | 15 | % | ISO 527-2/50 |
| Break, 23°C | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 2530 | MPa | ASTM D790 |
| 23°C 1 | 2480 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C 2 | 72.0 | MPa | ISO 178 |
| Yield | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | |||
| -18°C 3 | 14 | kJ/m² | ASTM D256 |
| -18°C 4 | 12 | kJ/m² | ISO 180 |
| 23°C 5 | 29 | kJ/m² | ISO 180 |
| 23°C 6 | 48 | kJ/m² | ASTM D256 |
| Multi-Axial Instrumented Impact Energy | ASTM D3763 | ||
| -18°C, 40.0 mm, Energy to Peak Force | 26.0 | J | |
| -18°C, 40.0 mm, Total Penetration Energy | 30.0 | J | |
| 23°C, 40.0 mm, Energy to Peak Force | 20.0 | J | |
| 23°C, 40.0 mm, Total Penetration Energy | 33.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Annealed 7 | 95.1 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 94.5 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ASTM D1525 8 |
| -- | 94.1 | °C | ISO 306/B50 |
| -- | 97.0 | °C | ISO 306/B120 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.10 mm, White | HB | ||
| 1.50 mm, All Colors | HB |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 20° | 87 | ||
| 60° | 96 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 12.7-mm x 3.2-mm, 0.25-mm notch |
| 4 . | 10.0-mm x 4.0-mm, 0.25-mm notch |
| 5 . | 10.0-mm x 4.0-mm, 0.25-mm notch |
| 6 . | 12.7-mm x 3.2-mm, 0.25-mm notch |
| 7 . | Annealed 2 hours at 80°C |
| 8 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7716 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Synthos PS GP 545 | Synthos S.A. | PS (GPPS) | Synthos PS |
| FERREX® GPP30CS81HB NATURAL | Ferro Corporation | PP Copolymer | FERREX® |
| INSTRUC PPGF30CC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |
| Karina CLEAR PVC COMPOUND 70850/200-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |