ColorFast® PBA1000
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GDeq3G_ColorFast-PBA1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/ABS alloy with excellent physical properties and chemical resistance |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 46.9 | MPa | |
| Break | 33.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 35 | % | |
| Flexural Modulus 3 | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 204 to 238 | °C | |
| Middle Temperature | 210 to 232 | °C | |
| Front Temperature | 221 to 254 | °C | |
| Nozzle Temperature | 216 to 249 | °C | |
| Processing (Melt) Temp | 221 to 254 | °C | |
| Mold Temperature | 10.0 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-101G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| APEX® 1565 | Teknor Apex Company | PVC, Flexible | APEX® |
| DOMAMID® 66G15FC | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Pearlthane® D11H95S | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| Bapolene® 4062NA | Bamberger Polymers, Inc. | PP Homopolymer | Bapolene® |