| Extrusion grade, high impact, high gloss ABS |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 35.9 | MPa | |
| Break | 27.6 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 110 | % | |
| Flexural Modulus 3 | 1720 | MPa | ASTM D790 |
| Flexural Strength 4 | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 82.8 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 30 to 60 | % | |
| Rear Temperature | 188 to 210 | °C | |
| Middle Temperature | 204 to 227 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Nozzle Temperature | 218 to 260 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| INSTRUC PESGF30 | Infinity LTL Engineered Compounds | PESU | INSTRUC |
| JSR EPR EP57P | JSR Corporation | EPDM | JSR EPR |
| Maxxam™ PP5120F B2 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Sylvin 913-80 White 1491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |