LEXAN™ XHT5141 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GCzm5E_LEXANXHT5141resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XHT5141 is a high flow, high heat polycarbonate copolymer with a haze onset of 185C. It is available in a range of opaque colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.95 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 80.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 65.0 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.5 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture 5 | 45 | % | ASTM D638 |
| Fracture | 45 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2650 | MPa | ASTM D790 |
| -- 7 | 2550 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 120 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -30°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 185 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 14 | 183 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 174 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 170 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 190 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 16 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 165°C | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (25°C) | 0.20 | W/m/K | ASTM C177 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 185 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 5.0 - 6.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 300 - 325 | °C | |
| Middle Temperature | 310 - 335 | °C | |
| Front Temperature | 320 - 345 | °C | |
| Nozzle Temperature | 315 - 340 | °C | |
| Processing (Melt) Temp | 320 - 345 | °C | |
| Mold Temperature | 110 - 140 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ GLT65 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Synres® PP 70 MH13 MB | Teknor Apex Company | PP, Unspecified | Synres® |
| Nanjing Hongrui PA6 B1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| HANWHA KH-10 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| LUVOCOM® 80-8003 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |