ELITE™ CS 6085B
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GCefss_ELITE-CS-6085B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE CS 6085B Enhanced Polyethylene Resin is an enhanced LLDPE ethylene-octene copolymer from Dow. This grade is a fully formulated resin designed for FFS and lamination films, combining excellent optical properties with improved mechanicals and an additive package designed to enhance COF stability. Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With self-dynamics | 0.091 | ASTM D1894 | |
| With Self-Static | 0.11 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Resistance (50 µm) | 6.62 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 165 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 8.70 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 9.40 | MPa | ASTM D882 |
| MD : Break, 50 µm | 30.3 | MPa | ASTM D882 |
| TD : Break, 50 µm | 28.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 700 | % | ASTM D882 |
| TD : Break, 50 µm | 750 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 640 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 920 | g | ASTM D1922 |
| TD : 50 µm | 1200 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 54 | ASTM D2457 | |
| Haze (50.8 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 239 | °C |
| Extrusion instructions |
|---|
| RPM/min: 40 Pressure: 146 Bar Blow-up Ratio: 2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 321 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Sylvin 9812-70 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WPP PP JOSB26624 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| ALCOM® PA66 910/1.1 CF10 GF10 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| ATTANE™ SL 4102G | The Dow Chemical Company | ULDPE | ATTANE™ |