Aegis® BarrierPro2™
| Category: | HPPA , High Performance Polyamide |
| Manufacturer: | Honeywell |
| Trademark: | Aegis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GBktTQ_Aegis-BarrierPro2-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aegis® HFX is an oxygen scavenging polyamide composition formulated specifically for use in high performance packaging applications where high gas barrier is required. This product is useful in injection and extrusion molding applications. Aegis® HFX offers high oxygen barrier, even at high humidity, outstanding delamination resistance and whitening resistance, clarity and easy processing (particularly in the PET co-injection stretch blow molding process). |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.73 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 260°C/2.16 kg | 13 | g/10 min | ISO 1133 |
| 280°C/2.16 kg | 23 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 83.4 | MPa | ISO 527-2 |
| Fracture | 51.4 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.2 | % | ISO 527-2 |
| Fracture | 190 | % | ISO 527-2 |
| Flexural Modulus | 2540 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Transmission Rate (23°C, 80% RH, cast film) | < 0.033 | cm³/m²/24 hr | ASTM D3985 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 72.5 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.8 | °C | ASTM D648 |
| Glass Transition Temperature | 81.0 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 245 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 265 | °C | |
| Nozzle Temperature | 265 | °C |
| Injection instructions |
|---|
| Feed Zone: 35°CManifold: 265 to 280°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL EF-6133L2 | Teknor Apex Company | TPE | Telcar® |
| VITAMIDE® BI12NT6527 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TRAMID® 4110G15 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| BJB Silicone TC-5050 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| Zytel® LC7602 BK010A | DuPont Performance Polymers | Nylon, Unspecified | Zytel® |