Vyncolit® E 8353-706R Datasheet,Epoxy,Vyncolit N.V.-SHANGHAI SUSHENG

Message
E 8353-706R is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability good strength at elevated temperatures.

General Information
Filler / Reinforcement	Glass \Mineral
Features	Good dimensional stability The degassing effect is low to no Low viscosity Solvent resistance Anti-salt water/fog Good thermal shock resistance Good strength Good chemical resistance alkali resistance acid resistance Non-corrosive
Uses	Electrical components Military application Connector
Agency Ratings	FDA not rated USDA Unspecified Approval
Appearance	Black
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.98	g/cm³	ASTM D792
Molding Shrinkage - Flow (Compression Molded)	0.50	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	72.0	MPa	ASTM D638
Flexural Modulus (Compression Molded)	18000	MPa	ASTM D790
Flexural Strength (Break)	114	MPa	ASTM D790
Compressive Strength	235	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	22	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded)	282	°C	ASTM D648
CLTE - Flow	2.5E-5	cm/cm/°C	ASTM E831
Thermal Conductivity	0.60	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	16	kV/mm	ASTM D149
-- ²	14	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	4.50		ASTM D150
Dissipation Factor (1 MHz)	0.010		ASTM D150
Arc Resistance	180	sec	ASTM D495

Injection	Nominal Value	Unit
Middle Temperature	60.0 - 82.2	°C
Nozzle Temperature	82.2 - 93.3	°C
Processing (Melt) Temp	93.3 - 116	°C
Mold Temperature	149 - 177	°C
Injection Pressure	34.5 - 68.9	MPa
Holding Pressure	13.8 - 34.5	MPa
Back Pressure	0.345	MPa

Injection instructions
Gauge: 0.3The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.14%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°CDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 14.2 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 16.4 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method B, dry: 15.2 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, dry: 17.1 kV/mmDielectric Constant, ASTM D150, 1000000 Hz, wet: 4.5Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.01Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 225 °F Mold Temperature: 325 to 370 °F Compression Mold Pressure: 1000 to 5000 psi Transfer Mold Pressure: 1500 to 8000 psi Cure Time, 0.125 in: 60 to 90 sec

Injection instructions

Gauge: 0.3The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM C518.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.14%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°CDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 14.2 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 16.4 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method B, dry: 15.2 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, dry: 17.1 kV/mmDielectric Constant, ASTM D150, 1000000 Hz, wet: 4.5Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.01Compression and Transfer Molding Conditions: Preheat Temperature: 180 to 225 °F Mold Temperature: 325 to 370 °F Compression Mold Pressure: 1000 to 5000 psi Transfer Mold Pressure: 1500 to 8000 psi Cure Time, 0.125 in: 60 to 90 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GBX9R8_Vyncolit-E-8353-706R.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
tefanyl® VE VEIP 204	Mitsubishi Chemical Performance Polymers, Inc.	PVC, Flexible	tefanyl® VE
Complet® LCF30-PA66 MT	PlastiComp, Inc.	Nylon 66	Complet®
Gallonprene® GP540-9004	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Peripor® 200 E	BASF Corporation	PS (EPS)	Peripor®
TECHNYL® A 20 V25 BLACK 2006 CF	Solvay Engineering Plastics	Nylon 66	TECHNYL®