CALIBRE™ 503-5 TINT
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GBLSDf_CALIBRE-503-5-TINT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 503-5 Polycarbonate resin offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to medium complexity, such as five wall sheet. CALIBRE 503-5 is a polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 503-5 is specially designed to offer a significantly better sheet surface quality at higher line speeds than a standard linear polycarbonate resin such as CALIBRE 302-5, and has a reduced tendency to display chatter marks. CALIBRE 503-5 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 3 | 73.0 | MPa | ASTM D638 |
| Break | 73.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2350 | MPa | ASTM D790 |
| -- 6 | 2350 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 94.0 | MPa | ASTM D790 |
| -- 8 | 94.0 | MPa | ISO 178 |
| Taber Abrasion Resistance 9 | 20 | % | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 83 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 370 | J/m | |
| 23°C | 930 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 147 | °C | Internal Method |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ASTM D1525, ISO 306/B50 6 10 |
| -- | 151 | °C | ASTM D1525, ISO 306/A120 7 11 |
| CLTE - Flow (-40 to 80°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 86.0 to 90.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Method I (3 point load), 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | CS10F Wheel, 250 g, 300 cycles |
| 10 . | Rate A (50°C/h), Loading 2 (50 N) |
| 11 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ BN31 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| apigo® 9160 NL/90 | API SpA | TPO (POE) | apigo® |
| Gallonprene® GP540-7005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| StarFlex® 7025-1104 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |
| NORYL™ WCA871A resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |