Jackdaw PLA HW10NT6624
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PLA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAkyB0_Jackdaw-PLA-HW10NT6624.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PLA HW10NT6624 is a Polylactic Acid (PLA) product. It can be processed by extrusion and is available in Europe. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.40 | % | |
| Flow | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 75 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Stress | |||
| Break | 16.0 | MPa | ISO 527-2 |
| -- | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 250 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 50.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 148 | °C | ISO 1218, ASTM D2117 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANTEX® 630N | Nantex Industry Co., Ltd. | NBR | NANTEX® |
| ADEKA NS-2400 | Adeka Corporation | PUR-Ester | ADEKA |
| Iupilon® GSH2030R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| PSM® HL-101-40 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |
| PENTAMID AB GV50 H black | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |