POCAN® B 3233 HR 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAYkOo_POCANB3233HR000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30 % glass fibers, injection molding, improved flowability, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 260°C, 2.00mm 1 | 1.0 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | % | ISO 2577 |
| Flow direction : 260°C, 2.00mm 3 | 0.30 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 125 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 9100 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 200 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.2 | % | ISO 178/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behavior 8 | passed | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMRW, 09-100, GF30 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 55 | kJ/m² | ISO 180/1U |
| 23°C | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Melting Temperature 9 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 800 | °C | IEC 60695-2-12 |
| 1.50 mm | 800 | °C | IEC 60695-2-12 |
| 3.00 mm | 800 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 825 | °C | IEC 60695-2-13 |
| 1.50 mm | 825 | °C | IEC 60695-2-13 |
| 3.00 mm | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VS410 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| Clariant Nylon 6/6 6603-HSL | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Fiberfil® J-69/10/E/UV | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Karina GRAY COLOR CONCENTRATE 18/387-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ ML7696 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |