LNP™ STAT-KON™ SX90398 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAOB7V_LNP-STAT-KON-SX90398-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* SX90398 is a compound based on Nylon 12 resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-S-90398 Product reorder name: SX90398 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.1 | % | |
| Across Flow : 24 hr | 1.7 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1910 | MPa | ASTM D638 |
| -- | 1440 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 44.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2 |
| Break | 36.1 | MPa | ASTM D638 |
| Break | 35.0 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.3 | % | |
| Break | 120 | % | |
| Flexural Modulus | |||
| -- | 1780 | MPa | ASTM D790 |
| -- | 1760 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 62.4 | MPa | ASTM D790 |
| -- | 50.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 85 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.73 | J | ASTM D3763 |
| -- | 20.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 114 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 104 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 67.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 73.8 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 232 to 243 | °C | |
| Processing (Melt) Temp | 204 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B20 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Bapolene® PP5063 | Bamberger Polymers, Inc. | PP Random Copolymer | Bapolene® |
| Generic Nylon 12 - Unspecified | Generic | Nylon 12 | Generic |
| HAIPLEN EP10 G4 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Sylvin 8754-60FUV Orange 576 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |