KIBISAN® PN-137H
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBISAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GADwy9_KIBISAN-PN-137H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KIBISAN® PN-137H is a Styrene Acrylonitrile (SAN) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.90 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 6.35 mm) | 85 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 166 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 82.0 | MPa | ISO 527-2/50 |
| Break | 82.0 | MPa | ISO 527-2/50 |
| 3.18 mm 1 | 76.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.18 mm 2 | 7.0 | % | ASTM D638 |
| Break | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.35 mm 3 | 3730 | MPa | ASTM D790 |
| -- 4 | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 5 | 118 | MPa | ASTM D790 |
| -- 6 | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 23 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 20 | J/m | ASTM D256 |
| -- | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180/1U |
| Impact Flexural Test | DIN 53453 | ||
| Notched | 4.00 | kJ/m² | |
| Unnotched | 25.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm 7 | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 91.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 6.35 mm 8 | 103 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525 9 |
| -- | 109 | °C | ISO 306/A50 |
| -- | 111 | °C | ISO 306/A120 |
| -- | 105 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 120°C/hr |
| 8 . | 120°C/hr, Annealed at 85°C for 8 hr |
| 9 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 540500A65 | SO.F.TER. SPA | SBS | Sofprene T® |
| ExxonMobil™ PP7033L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| EPLAMID 66 GFS 20 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| HiFill® PA6 0137 S2 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Infino SC-1220UR | SAMSUNG SDI CO., LTD. | PC | Infino |