Order Products : sales@su-jiao.com
ULTEM™ 1010F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GABNbS_ULTEM1010Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ULTEM 1010F resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94 V0, V2 and 5VA ratings and is RoHS compliant. ULTEM 1010F resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures with easy flow. This grade is US FDA and EU Food Contact compliant. ULTEM 1010F resin is not supported with biocompatibility information. For medical applications which require biocompatibility we offer ULTEM HU1010 resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3590 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3520 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 165 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 1200 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 33.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 207 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 199 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 6 |
| CLTE - Flow (-20 to 150°C) | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 33 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 2.45 GHz | 2.5E-3 | ASTM D150 | |
| Arc Resistance 7 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Oxygen Index | 44 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 2.00 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Injection Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| NuSil G-9340 | NuSil Technology | Silicone | NuSil |
| Desmoderm® KCW | Covestro - PUR | PUR-Ester | Desmoderm® |
| LNP™ LUBRICOMP™ RFN1ASXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Osterlene® HI-8-2-hg | Osterman & Company | PS (HIPS) | Osterlene® |