Toppyl SP 2103 C

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	LyondellBasell Industries
Trademark:	Toppyl
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	G9O3Ob_Toppyl-SP-2103-C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Toppyl SP 2103 C is a barefoot seal peel solution developed for the cast and blown film technology. This product has been designed to offer a peelable seal to PP substrates and is suitable for sterilisable applications. Toppyl SP 2103 C is a solution created to replace completely the sealing layer in a coextruded film. It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures. EU and FDA compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications.

Message

Toppyl SP 2103 C is a barefoot seal peel solution developed for the cast and blown film technology.

This product has been designed to offer a peelable seal to PP substrates and is suitable for sterilisable applications.

Toppyl SP 2103 C is a solution created to replace completely the sealing layer in a coextruded film.

It provides a constant easy-opening force over a wide sealing temperature window and is readily processable on conventional equipment in both mono and co-extruded structures.

EU and FDA compliance information about this product can be found in separate product documentation.

This product is not intended for use in medical and pharmaceutical applications.

General Information
Features	Semicrystallization Good heat sealability No additive
Uses	Films cast film
Agency Ratings	EU Unspecified Rating FDA not rated
Processing Method	Blow film Co-extruded film cast film

Physical	Nominal Value	Unit	Test Method
Density	0.902	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	6.0	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Secant Modulus - 2% Secant, MD	260	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield	15.0	MPa	ASTM D882
Fracture	33.0	MPa	ASTM D882
Tensile Elongation - MD (Break)	790	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	107	°C	ISO 306/A50

Additional Information
Recommended processing temperatures: 185°C to 265°C. In cases were higher temperatures are required please contact your appropriate technical contact for support.

Resin Grade	Manufacturer	Category	Trademark
CONAP® CE-1170	Cytec Industries Inc.	Acrylic, Unspecified	CONAP®
Dryflex® 662300S	ELASTO	SEBS	Dryflex®
Flontech® FT-BRR40-6	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
Karina WHITE PVC COMPOUND -E 855-10/150-ERYB-PO	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sylvin 4215-75 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin