Ultradur® B 4040 G11 HMG BK15029
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G8bQBX_Ultradur-B-4040-G11-HMG-BK15029.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur B 4040 G11 HMG BK15029 is a polybutylene terephthalate alloy reinforced with 55% glass fiber. In addition to high stiffness it offers exceptional dimensional stability. Applications Typical applications include automotive exterior components such as mirror brackets and wiper arms. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.81 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 21000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 163 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 47 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 11 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 219 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 TFE 15 | RTP Company | Nylon 66 | RTP |
| RIALENE® P 100 SGF20 ST F V-0 natural | RIA-Polymers GmbH | PP, Unspecified | RIALENE® |
| Spartech Polycom SC1-7010 | Spartech Polycom | ABS | Spartech |
| Hostaform® C 9021 XAP2 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ STAT-KON™ RD000I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |