Tufpet PBT G2630
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7gw1O_Tufpet-PBT-G2630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G2630 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber and 10% mineral. It is available in North America for injection molding. Important attributes of Tufpet PBT G2630 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 9320 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact | 470 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 186 | °C | |
| RTI Elec | UL 746 | ||
| 0.780 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.12 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.780 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.12 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 0.780 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.12 mm | 75.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 49.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 220 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.780 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.12 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B22^E F40 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Starex SR-0315 V | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Hifax CA 207 A | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| OmniPro™ HPP GRC25 CBFR0 | OMNI Plastics, LLC | PP, Unspecified | OmniPro™ |
| LNP™ THERMOCOMP™ GF006 compound | SABIC Innovative Plastics | PSU | LNP™ THERMOCOMP™ |