LNP™ THERMOCOMP™ QF008 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7bIFD_LNPTHERMOCOMPQF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound QF-1008 Product reorder name: QF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 | g/cm³ | ASTM D792 |
| -- | 1.42 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 12400 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture | 172 | MPa | ASTM D638 |
| Fracture | 183 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638 |
| Flexural Modulus | 10800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 219 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 208 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 214 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 A TFE 15 UV | RTP Company | Nylon 6 | RTP |
| S&E Battery GR-1409 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Battery |
| LNP™ THERMOCOMP™ RF0079SZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| HIFOR Xtreme® SC74869 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| ESTOPLAST EP 4030HG38 | Ester Industries Ltd. | PBT | ESTOPLAST EP |