| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7UsEO_LNPLUBRICOMPDL0029Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DL0029E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DL-4020 FR Product reorder name: DL0029E |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 24.0 - 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.70 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 56.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 5.1 | % | ISO 527-2/5 |
| Flexural Modulus 2 | ISO 178 | ||
| -- | 2700 | MPa | ISO 178 |
| 60°C | 1400 | MPa | ISO 178 |
| 100°C | 700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 82.0 | MPa | ISO 178 |
| 60°C | 35.0 | MPa | ISO 178 |
| 100°C | 18.0 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.32 | ASTM D3702 Modified | |
| Flexural Strain at Break 3 | ISO 178 | ||
| -- | 7.0 | % | ISO 178 |
| 60°C | 7.0 | % | ISO 178 |
| 100°C | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 16.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 140 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, unannealed, 64.0mm span | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 128 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.70 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 801 CC TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| APEX® 1527 | Teknor Apex Company | PVC, Flexible | APEX® |
| Colorite G Series 9511G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Hy-Vin® XH79026 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Starex NH-0925 S | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |