Ingeo™ 6752D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7SIhu_Ingeo-6752D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo biopolymer 6752D, a NatureWorks LLC product, is a thermoplastic fiber-grade resin derived from annually renewable resources. Available in pellet form, 6752D is designed for extrusion into mechanically drawn staple fibers using conventional fiber spinning and drawing equipment. Ingeo biopolymer 6752D can be converted into a broad range of un-dyed products. See table at right for typical properties. Applications Potential applications for Ingeo biopolymer 6752D include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Contractility- Hot Air 1(120°C) | % | ASTM D2102 | |
| Relative Viscosity | 3.30 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| modulus of elasticity | 20.0 - 40.0 | g/denier | ASTM D2256 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Denier - per filament 2 | > 1.50 | ||
| Elongation of Fibers | 10 - 70 | % | ASTM D2256 |
| Tenacity of Fibers | 2.50 - 4.00 | g/denier | ASTM D2256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 - 60.0 | °C | ASTM D3417 |
| Peak Crystallization Temperature (DSC) | 145 - 160 | °C | ASTM D3418 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (230°C) | 1.08 | g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | < 5.0E-3 | % | |
| Melt Temperature | 220 - 240 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 24:1 to 30:1Compression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | 10 min |
| 2 . | g/9000m |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vandar® 2100 | Celanese Corporation | PBT | Vandar® |
| NaturePlast NP WF 004 | NaturePlast | Biodeg Polymers | NaturePlast |
| ANSALON A08 000 0000 V0 HF | Daloga srl | PC | ANSALON |
| Ferro PP LPP10BK38BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| King Pearl® G-P | Loyal Chemical | PS (EPS) | King Pearl® |