LG ASA LI942
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7OOVh_LG-ASA-LI942.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ASA LI942 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG ASA LI942 are:
Typical application of LG ASA LI942: Automotive |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Moisture Content | > 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 88 | J/m | |
| 23°C, 6.40 mm | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 99.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 5 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 50.0 | °C | |
| 3.00 mm | 50.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 50.0 | °C | |
| 3.00 mm | 50.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 50.0 | °C | |
| 3.00 mm | 50.0 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 210 to 240 | °C | |
| Front Temperature | 220 to 250 | °C | |
| Nozzle Temperature | 220 to 250 | °C | |
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 68.6 to 88.3 | MPa | |
| Screw Speed | < 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer Pipe PP 410/401 | Polylink Polymers (India) Ltd. | PP, Unspecified | Polylink Polymer |
| VICOTE® F804 | Victrex plc | PEEK | VICOTE® |
| Toyolac® 125-X82 | Toray Resin Company | ABS | Toyolac® |
| Flexathene® TP4390HU | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Edgetek™ PC-20GF/000 FR BK | PolyOne Corporation | PC | Edgetek™ |