| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7Icp5_PLUSTEK-PB304G7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Fiber Reinforced, Heat Stabilized and Impact Modified Polyamide 6 for Injection Moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.15 - 0.35 | % | ASTM D955 |
| -- | 0.15 - 0.35 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 7.0 | % | ASTM D570 |
| Saturated, 23°C | 7.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.3 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 122 | ASTM D785 | |
| R scale | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 195 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 300 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| 23°C | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 200 | °C | |
| Maximum Continuous Use Temperature | 110 | °C | |
| Melting Temperature | 218 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V75G | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Propilven F-605 | Propilven, S.A. | PP Homopolymer | Propilven |
| SABIC® PP CX03-82 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PP |
| TAIRIREX GP5500 | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| LNP™ LUBRICOMP™ OCP36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |