Shinite® PBT D201G30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shinkong Synthetic Fiber Corp. |
| Trademark: | Shinite® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7GEmT_Shinite-PBT-D201G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinite® PBT D201G30 is a Polybutylene Terephthalate (PBT) material filled with 30% glass fiber. It is available in North America. Important attributes of Shinite® PBT D201G30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 1.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11900 | MPa | ASTM D638 |
| Tensile Strength | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 8480 | MPa | ASTM D790 |
| Flexural Strength | 189 | MPa | ASTM D790 |
| Compressive Strength | 157 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 208 | °C | ASTM D648 |
| Melting Temperature | 224 | °C | DSC |
| CLTE - Flow | 3.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 29 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.20 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 232 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 241 to 260 | °C | |
| Mold Temperature | 60.0 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 D TFE 15 | RTP Company | Nylon 612 | RTP |
| Toler EVA 182 | Toler Chemical, Inc | EVA | Toler EVA |
| Jiangsu Sinarise ZM928 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina BLACK PVC COMPOUND -E 855-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ LCL33EXQ compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |