Crastin® HR5330HF NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G7D6Ww_Crastin-HR5330HF-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Hydrolysis Resistant, Polybutylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.35 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.15 | % | |
| Viscosity Number | 95.0 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 132 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 7700 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 11 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 221 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| -- | 31 | kV/mm | |
| 1.00 mm 2 | 31 | kV/mm | |
| Relative Permittivity (100 Hz) | 4.40 | IEC 60250 | |
| Dissipation Factor | |||
| 100 Hz | 2.5E-3 | ASTM D150, IEC 60250 | |
| 1 kHz | 7.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index | 375 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 30 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 19 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.29 | g/cm³ | |
| Specific Heat Capacity of Melt | 1730 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.28 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6091 B-60A NATURAL | RTP Company | TPV | RTP |
| ABS Proquigel AM | Proquigel | ABS | ABS Proquigel |
| Hanwha Total PP GH42 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Honeywell PCTFE P900TR | Honeywell | PCTFE | Honeywell PCTFE |
| Petrothene® GA502023 | LyondellBasell Industries | LLDPE | Petrothene® |