RIALBATCH H 15 65 C
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALBATCH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | G71007_RIALBATCH-H-15-65-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound filled with 65% calcium carbonate. Application suggested as a masterbatch in furnishing. Available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.75 | % | |
| Flow | 0.75 | % | |
| Ash Content | 65 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 13.0 | MPa | ISO 527-2/20 |
| Tensile Strain (Yield, 23°C) | 2.0 | % | ISO 527-2/20 |
| Flexural Modulus 1(23°C) | 4500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 23.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pomalux® Unfilled | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| Braskem PP EP 448S | Braskem | PP Impact Copolymer | Braskem PP |
| Envirez® L 56307 resins | Ashland Performance Materials | Polyester, TS | Envirez® |
| TECHNYL® AZ 536 V20 BLACK | Solvay Engineering Plastics | PPE+Nylon 66 | TECHNYL® |
| NORYL™ 731 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |